Average Size 1MM * Range (0.5 to 3MM)
FRACTALBALLS may be used as thermal insulation, chemical substrates or as structural materials when bonded with FRACTAL PASTE or FRACTALGLUE.
Use as thermal insulation: FRACTALBALL have very low density, low thermal conductivity, high strength, and high melting point; as they are free flowing they can be formed into any shape and size and be used for refractory/insulation parts for high and low temperature application. (to form a rigid part they have to be mixed with fractalpaste and fired in a furnace after drying).
Typical applications are: thermal insulation, fire protection and stops, high temperature furnace linings, kiln furniture, and gas combustion burners. A very common use is for repairing or relining refractory cracks and holes.
Use for high surface reactivity: FRACTALBALLS have very high porosity/low density, high strength, and high melting point. They may be used for high temperature filter and membrane substrate applications.
Typical applications are: Light weight structure materials. Composite manufacture reinforcement additive for metal, ceramic, or polymer. Armor, bio-ceramic, abrasive brake pads etc. Coatings for surfaces (Metals, Ceramics, polymers.)
Other typical applications are: Filter molten metal castings (aluminum, copper, iron). Steam cleaning. Apply as light weight coatings or Oil trapping and recovery, grease filters. Chemical and water purification processes. Hot-gas filters substrates for electrode. Electronic substrates carriers for bioreactors. Desiccants Substrates for catalytic converters. Usage as light weight structural materials. FRACTALBALL has an unique microstructure, very low density, high strength, and high hardness.
All trade marks on this document belong to MATTECH CORPORATION unless otherwise stated.
FRACTALBALL is a unique, lightweight, non-hollow porous ball with a very low density and high strength (not all porosity is connected). The material of the FRACTALBALLS (called HMG1) has excellent heat, chemical and mechanical stability; the spheres have low thermal conductivity and high thermal shock resistance. The spheres are sold in a fully fired condition with excellent dimensional stability up to 1900C. FRACTALBALLS are environmental-friendly materials: they do not contain any hazardous materials such as organic volatents, or fibrous materials, and will not produce any smoke or odor when heated. They also have desirable chemical, physical and mechanical properties, such as inertness to chemical attack (solvents, acids, alkalies, and detergents), non-wettability by molten metals such as aluminum, high thermal stability, high strength, and micro-biological stability. These features permit the FRACTALBALLS to be used in various applications.
FRACTALBALLS, which are made from the HMG1 material may be used in loose stacked form or bonded into any size and shape part by bonding the FRACTALBALLS with FRACTALGLUE. These flexible processing possibilities allow FRACTALBALLS to be use in various technologies.
Properties of Material HMG1 – Color – White Nominal Composition,wt % Mullite – 90% Al203 – 10% Other Metal – less than 1% Ball Density, g/cc – 1.0 Stacked Density,g/cc – 0.7 Diameter,mm – (major range 1-4 mm) Maximum Use Temperature,°C -1900° C Ball Porosity, % (average) – 70 Strength – Each 3mm ball supports approximately 10Kg of Load. High Strength. Normally supplied as hydrophobic surface. Special orders can be made to change this. to hydrophyllic.
FRACTALBALLS have a porosity of about 70%, when loosely stacked the porosity is about 85%, Fractalglue bonded Fractalballs have a porosity of 75% whereas FRACTALINS have a porosity of about 80%. Factallballs glued with Fractalglue has a strength of 5MPa whereas FRACTALINS have a strength of about 6MPa.
The composition of HMG1 material is given by clicking on Technical Data link. MSDS sheets may also be downloaded from the site. Patents Applied For And Pending. FRACTALBALLS, FRACTALINS , FRACTALGLUE,FIBERFREE,and FRACTALBALL are trademarks of MATTECH CORPORATION.